| fep lc200 technical parameter： | |||
| physical performance | specific gravity | g/cm3 | 2.12-2.17 |
| melting flow rate | g/10min | 30 | |
| melting point | ℃ | 265±10 | |
| mechanical performance | tensile strength | mpa | ≧15 |
| breaking extension | % | ≧200 | |
| hardness | shore hardness | 56 | |
| yield strength | mpa | - | |
| coefficient of dynamic friction | —— | 0.3 | |
| thermal performance | maximal temperature of continuous work | ℃ | 200 |
| thermal distortion temperature | ℃（ 1.82mpa） | 47 | |
| coefficient of linear expansion | (-10-5/℃） | 8-15 | |
| electrical performance | volume resistanc | ω.cm | >1018 |
| insulation breakdown voltage | kv(3.2mm thickness) | 20 | |
| relative dielectric constant | 1khz | 2.1 | |
| dielectric loss angle tangent value | 1khz | <0.0005 | |
| application fields | ultra fine electron wire, ultra fine rf coaxial wire high speed formation | ||
| extrusion application | ultra fine electron wire, coaxial wire (30awg-48awg) below 0.1 mm | ||